Glaxs is a high adhesion system for indoor and outdoor bonding of ceramic, porcelain, and similar surfaces.

Transparent Cartridge Glue

Available in a wide variety of colors. Requires use of special M200XMR Cartridge Gun.

GLAXS ADVANTAGES:

• VOC free
• Excellent adhesion
• Ultra rapid
• Excellent color stability to sunlight
• Glossy, shiny and easy to polish
• Indoor and Outdoor use
• Pre-dosed for easy dispensing
• Comes with 2 mixing nozzles

GLAXS CLEAN WHITE INSTRUCTIONS FOR USE:

1. All the surfaces to be treated must be cleaned and free of dust and grease.
2. In case of glossy and/or smooth surfaces, we suggest scrubbing the surfaces with sandpaper before gluing.
3. Remove the threaded extremity and uncap the cartridge.
4. Fix the mixer to the cartridge through the threaded nozzle.
5. Before applying the glue on the surfaces, do spurge around 5 gr in line.
6. Use only guns approved by Tenax, MK Sulzer ratio 2+1 H236M and Mixpac DM200-01 ratio 2+1.
7. After usage, clean the nozzle, replace the cap and discard the mixer after use. Product will not set below +1C.

SHELF LIFE:

Glaxs Clean White in cartridge will last at least 12 months, in normal conditions between 18-25c, kept away from source of heat, humidity and sun light.

SAFETY RULES:

Resin and hardener are chemical products, please read the safety data sheet before usage and the rules written on the product label.

• Gel time in bulk at 77: 3-5 min
• Tacky free time at 77: approx. 15 min
• Working time at 77: 45-60 min
• Temp range for use after hardening: -13F to 140F

Viscosity cps 25C 20 r.p.m (ASTM D2196) tixotropic liquid Density at 25C gr/cm3 1.27 Aspect colored liquid Ratio of use glue/hardener 2+1 Gel time (in bulk) at 25C in min 3-5 min Time for handling pieces 15-20 min Working time suggested at 25C in min 45-60 min Minimum reaction temperature +1C Minimum temperature of use after hardening -25C Minimum temperature of use after hardening +60C Shelf life at 18-20C 24 months Adhesion force in MPa at 25C on natural stone, diamond cut surface after 1 hour (ASTM D 4541)* 9.0 – 10.0 Adhesion force in MPa at 25C on natural stone, diamond cut surface after 24 hours (ASTM D 4541)* 9.5 – 10.5 Adhesion force in MPa at 25C on quartz, diamond cut surface after 1 hour (ASTM D 4541)* 9.0 – 10.0 Adhesion force in MPa at 25C on quartz, diamond cut surface after 24 hours (ASTM D 4541)* 12.0 – 13.0 Adhesion force in MPa at 25C on ceramic, diamond cut surface after 1 hour (ASTM D 4541)* 9.0 – 11.0 Adhesion force in MPa at 25C on ceramic, diamond cut surface after 24 hours (ASTM D 4541)* 10.0 – 13.0